What do you think makes the older steel harder than the new steel? I have a hard time believing it's the composition so it must be work-hardening from cold rolling or forming. Cold rolled steel is hardened by the rolling process. Perhaps they're now annealing the steel after cold-rolling or using hot-rolled and pickled steel so it forms easier.